Introduction:

This product adopts epoxy resin, functional curing agent, this product has high reactivity, strong adhesive force, high crosslinking density, the coating has excellent chemical resistance, solvent resistance, resistance to cathodic stripping, excellent flexibility, impact resistance and other properties.

Feature:

1. Very good adhesion with the substrate.

2. Good leveling, high gloss coating surface

3. Strong permeability and corrosion resistance

4. The coating has excellent high temperature cathodic disbonding resistance.

5. High surface hardness, strong coating density.

6. Low melting temperature, high reactivity, high curing completion rate.

7. Good mechanical performance, strong flexibility

Power Specification:

Test Items	Technical Indicators	Test Method
Appearance	Even color, no caking	visual
Colour	As customer required	visual
density（g/cm³）	1.3-1.5	GB/T 4472
Particle size distributor	150μm Sieve the powder	≤3.0	GB/T 6554-1986
250μm Sieve the powder	≤0.2	GB/T 6554-1986
non-volatile matter content (%)	≥ 99.4	GB/T 6554-1986
Gel time（s）	≤ 180s (180℃) ≤ 120s (200℃) ≤ 60s (230℃)	GB/T 6554-1986
magnetic material content（%）	≤ 0.002	GB/T 2482-1986
Level of liquidity（mm）	22~28	GB/T 6554-1986

Coating Specification

Test Items	Technical Indicators	Test Method
Appearance	smooth，uniform color, no bubble , no cracking and sinkhole, allow light crack	visual
Adhesion	1~3	SY/T 0442-1997
cathodic disbanding resistance 65℃48h（mm）	≤8	SY/T 0413-95
counter bending（40）	No cracking	SY/T 0442-1997
Electric strength（MV/m）	≥ 30	GB/T 1408-1989
Impact strength	≥ 11	SY/T 0442-1997
Resistance to chemical corrosion medium	10% HCL normal temperature90d 10%H2So4 normal temperature 90d 3.5% Nacl normal temperature 90d 10%NaOH normal temperature 90d	Qualified	GB/T1763-1979
oilfield sewage 80℃ 90d crude 80℃90d gas normal temperature 90d diesel normal temperature 90d kerosene normal temperature 90d	Qualified	GB/T 1733-1993
abrasive resistance 1000g.1000turn	≤20g	GB/T 1768-1979
Salt spray test（1000h）	No change	GB/T1771-1991
Flatten test (flatten ratio 4/5)	No cracking	CJ/T 120-2008

Carried Standard: SY/T 0442-97

Application Area: Municipal, water supply, drainage, sewage, circulating water, chemical, thermal and other pipelines.

Applicable process: Electrostatic Coating, inhale coating, dip coating, roller coating

Notes:

1. Steel surface should be no oil and water, surface quality should reach Sa2 1/2 level (GB/T8923), anchor pattern depth 50-90mm, clean dust and abrasive attached to the steel surface, preheat, control temperature in 180－230℃.

2. Product should be stored in ventilated, dry, indoor temperature below 30 ℃, away from heat, corrosive chemicals and chemical solvents, avoid bright light, the maximum stack height should not exceed 4 layers, avoid prolonged pressure, ensure airtight box. In case the clot and damp affects the fluidization performance.

3. To best curing epoxy coating, best anti-corrosion, suggested preheating tube surface temperature in more than 170℃, in order to better improve the curing completion.